| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.05
|
g/cm³
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)
|
18
|
g/10 min
|
ASTM D1238 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength 2 (Yield, 3.18 mm)
|
41.6
|
MPa
|
ASTM D638 |
|
Tensile Elongation 2 (Break, 3.18 mm)
|
2.0
|
%
|
ASTM D638 |
|
Flexural Modulus 3 (6.35 mm)
|
3030
|
MPa
|
ASTM D790 |
|
Flexural Strength 3 (6.35 mm)
|
52.9
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact
|
ASTM D256 | ||
|
23°C, 3.18 mm
|
15
|
J/m
|
|
|
23°C, 6.35 mm
|
14
|
J/m
|
|
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (M-Scale, 6.35 mm)
|
74
|
ASTM D785 | |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm)
|
75.0
|
°C
|
ASTM D648 |
|
Vicat Softening Temperature
|
87.0
|
°C
|
ASTM D1525 4 |
| Processing Information | |||
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80.0
|
°C
|
|
|
Drying Time
|
2.0 to 3.0
|
hr
|
|
|
Rear Temperature
|
150 to 170
|
°C
|
|
|
Middle Temperature
|
170 to 190
|
°C
|
|
|
Nozzle Temperature
|
175 to 195
|
°C
|
|
|
Mold Temperature
|
40.0 to 70.0
|
°C
|
|