**奇美ABS PA-758英文物性表
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.08
|
g/cm³
|
ASTM D792 |
|
Density
|
1.08
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
ASTM D1238 | ||
|
200°C/5.0 kg
|
3.0
|
g/10 min
|
|
|
220°C/10.0 kg
|
34
|
g/10 min
|
|
|
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
|
34.0
|
cm³/10min
|
ISO 1133 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength 2 (3.18 mm)
|
39.6
|
MPa
|
ASTM D638 |
|
Tensile Stress (Yield)
|
42.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Stress (Break)
|
33.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Strain (Break)
|
50
|
%
|
ISO 527-2/50 |
|
Flexural Modulus 3 (6.35 mm)
|
1860
|
MPa
|
ASTM D790 |
|
Flexural Modulus 4
|
1500
|
MPa
|
ISO 178 |
|
Flexural Strength 3 (6.35 mm)
|
53.6
|
MPa
|
ASTM D790 |
|
Flexural Strength 4
|
56.0
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
12
|
kJ/m²
|
ISO 179 |
|
Notched Izod Impact (23°C, 6.35 mm)
|
160
|
J/m
|
ASTM D256 |
|
Notched Izod Impact Strength
|
12
|
kJ/m²
|
ISO 180/1A |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Ball Indentation Hardness (H 358/30)
|
90.0
|
MPa
|
ISO 2039-1 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm)
|
87.8
|
°C
|
ASTM D648 |
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
85.0
|
°C
|
ISO 75-2/A |
|
Heat Deflection Temperature (1.8 MPa, Annealed)
|
96.0
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature 5
|
105
|
°C
|
ASTM D1525 6 |
|
Vicat Softening Temperature
|
|||
|
--
|
104
|
°C
|
ISO 306/A50 |
|
--
|
106
|
°C
|
ISO 306/A120 |
|
--
|
98.0
|
°C
|
ISO 306/B50 |
|
--
|
101
|
°C
|
ISO 306/B120 |
|
RTI Elec
|
UL 746 | ||
|
1.50 mm
|
60.0
|
°C
|
|
|
3.00 mm
|
60.0
|
°C
|
|
|
RTI Imp
|
UL 746 | ||
|
1.50 mm
|
60.0
|
°C
|
|
|
3.00 mm
|
60.0
|
°C
|
|
|
RTI Str
|
UL 746 | ||
|
1.50 mm
|
60.0
|
°C
|
|
|
3.00 mm
|
60.0
|
°C
|
|
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Arc Resistance
|
6.00
|
sec
|
ASTM D495 |
|
Comparative Tracking Index (CTI)
|
PLC 0
|
UL 746 | |
|
High Amp Arc Ignition (HAI)
|
UL 746 | ||
|
1.50 mm
|
PLC 3
|
||
|
3.00 mm
|
PLC 3
|
||
|
High Voltage Arc Tracking Rate (HVTR)
|
PLC 0
|
UL 746 | |
|
Hot-wire Ignition (HWI)
|
UL 746 | ||
|
1.50 mm
|
PLC 4
|
||
|
3.00 mm
|
PLC 3
|
||
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
1.50 mm, ALL
|
HB
|
||
|
1.59 mm
|
HB
|
||
|
3.00 mm, ALL
|
HB
|
||
| Optical |
Nominal Value
|
Unit
|
Test Method
|
|
Transmittance (3180 µm)
|
90.0
|
%
|
ASTM D1003 |
|
Haze (3180 µm)
|
4.0
|
%
|
ASTM D1003 |