**奇美ABS PA-765 英文物性
Physical |
Nominal Value
|
Unit
|
Test Method
|
Specific Gravity
|
1.19
|
g/cm³
|
ASTM D792 |
Density
|
1.19
|
g/cm³
|
ISO 1183 |
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)
|
5.0
|
g/10 min
|
ASTM D1238 |
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
|
49.0
|
cm³/10min
|
ISO 1133 |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Strength 2 (Yield, 3.18 mm)
|
38.1
|
MPa
|
ASTM D638 |
Tensile Stress (Yield)
|
39.0
|
MPa
|
ISO 527-2/50 |
Tensile Stress (Break)
|
34.0
|
MPa
|
ISO 527-2/50 |
Tensile Elongation 2 (Break, 3.18 mm)
|
15
|
%
|
ASTM D638 |
Tensile Strain (Break)
|
10
|
%
|
ISO 527-2/50 |
Flexural Modulus 3 (6.35 mm)
|
2070
|
MPa
|
ASTM D790 |
Flexural Modulus 4
|
1800
|
MPa
|
ISO 178 |
Flexural Strength 3 (6.35 mm)
|
60.8
|
MPa
|
ASTM D790 |
Flexural Strength 4
|
55.0
|
MPa
|
ISO 178 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
20
|
kJ/m²
|
ISO 179 |
Charpy Unnotched Impact Strength
|
No Break
|
ISO 179 | |
Notched Izod Impact
|
ASTM D256 | ||
23°C, 3.18 mm
|
210
|
J/m
|
|
23°C, 6.35 mm
|
180
|
J/m
|
|
Notched Izod Impact Strength
|
17
|
kJ/m²
|
ISO 180/1A |
Unnotched Izod Impact Strength
|
No Break
|
ISO 180/1U | |
Impact Flexural Test
|
|||
Notched
|
12.0
|
kJ/m²
|
ISO 179/2C |
Unnotched
|
No Break
|
ISO 179/2D | |
Hardness |
Nominal Value
|
Unit
|
Test Method
|
Rockwell Hardness (R-Scale, 12.7 mm)
|
100
|
ASTM D785 | |
Ball Indentation Hardness (H 358/30)
|
79.0
|
MPa
|
ISO 2039-1 |
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm)
|
72.8
|
°C
|
ASTM D648 |
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
74.0
|
°C
|
ISO 75-2/A |
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)
|
82.8
|
°C
|
ASTM D648 |
Heat Deflection Temperature (1.8 MPa, Annealed)
|
90.0
|
°C
|
ISO 75-2/A |
Vicat Softening Temperature
|
90.0
|
°C
|
ASTM D1525 5 |
Vicat Softening Temperature
|
|||
--
|
92.0
|
°C
|
ISO 306/A50 |
--
|
90.0
|
°C
|
ISO 306/A120 |
--
|
78.0
|
°C
|
ISO 306/B50 |
--
|
80.0
|
°C
|
ISO 306/B120 |
RTI Elec
|
UL 746 | ||
1.00 mm
|
80.0
|
°C
|
|
1.50 mm
|
80.0
|
°C
|
|
2.50 mm
|
80.0
|
°C
|
|
3.00 mm
|
80.0
|
°C
|
|
RTI Imp
|
UL 746 | ||
1.00 mm
|
80.0
|
°C
|
|
1.50 mm
|
80.0
|
°C
|
|
2.50 mm
|
80.0
|
°C
|
|
3.00 mm
|
80.0
|
°C
|
|
RTI Str
|
UL 746 | ||
1.00 mm
|
80.0
|
°C
|
|
1.50 mm
|
80.0
|
°C
|
|
2.50 mm
|
80.0
|
°C
|
|
3.00 mm
|
80.0
|
°C
|
|
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Volume Resistivity
|
1.0E+16
|
ohm·cm
|
IEC 60093 |
Arc Resistance
|
PLC 7
|
ASTM D495 | |
Comparative Tracking Index (CTI)
|
PLC 1
|
UL 746 | |
High Amp Arc Ignition (HAI)
|
UL 746 | ||
1.00 mm
|
PLC 0
|
||
1.50 mm
|
PLC 0
|
||
2.50 mm
|
PLC 0
|
||
3.00 mm
|
PLC 0
|
||
High Voltage Arc Tracking Rate (HVTR)
|
PLC 0
|
UL 746 | |
Hot-wire Ignition (HWI)
|
UL 746 | ||
1.00 mm
|
PLC 4
|
||
1.50 mm
|
PLC 2
|
||
2.50 mm
|
PLC 2
|
||
3.00 mm
|
PLC 0
|
||
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Flame Rating
|
UL 94 | ||
1.50 mm, ALL
|
|
||
1.60 mm
|
V-0
|
||
2.50 mm, ALL
|
|
||
3.00 mm, ALL
|
|
||
1.00 mm, ALL
|
V-1
|