专业供应ABS塑胶原料:电镀级ABS,透明ABS,透明级ABS,高透明ABS,食品级ABS,耐热ABS,耐高温ABS,耐候ABS,抗氧化ABS,抗紫外线ABS,抗UV ABS,耐热抗老化ABS,阻燃ABS,防火ABS,防火耐热ABS,透明食品级ABS,加玻纤ABS,等塑胶原料.
**奇美ABS PA-777E 英文物性表
Physical |
Nominal Value
|
Unit
|
Test Method
|
Specific Gravity
|
1.07
|
g/cm³
|
ASTM D792 |
Density
|
1.07
|
g/cm³
|
ISO 1183 |
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg)
|
4.0
|
g/10 min
|
ASTM D1238 |
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
|
4.00
|
cm³/10min
|
ISO 1133 |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Strength 2 (Yield, 3.18 mm)
|
45.0
|
MPa
|
ASTM D638 |
Tensile Stress (Yield)
|
44.0
|
MPa
|
ISO 527-2/50 |
Tensile Stress (Break)
|
37.0
|
MPa
|
ISO 527-2/50 |
Tensile Elongation 2 (Break, 3.18 mm)
|
10
|
%
|
ASTM D638 |
Tensile Strain (Break)
|
13
|
%
|
ISO 527-2/50 |
Flexural Modulus 3 (6.35 mm)
|
2210
|
MPa
|
ASTM D790 |
Flexural Modulus 4
|
2200
|
MPa
|
ISO 178 |
Flexural Strength 3 (6.35 mm)
|
68.3
|
MPa
|
ASTM D790 |
Flexural Strength 4
|
71.0
|
MPa
|
ISO 178 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
11
|
kJ/m²
|
ISO 179 |
Notched Izod Impact
|
ASTM D256 | ||
23°C, 3.18 mm
|
120
|
J/m
|
|
23°C, 6.35 mm
|
110
|
J/m
|
|
Notched Izod Impact Strength
|
11
|
kJ/m²
|
ISO 180/1A |
Unnotched Izod Impact Strength
|
95
|
kJ/m²
|
ISO 180/1U |
Hardness |
Nominal Value
|
Unit
|
Test Method
|
Rockwell Hardness (R-Scale, 12.7 mm)
|
115
|
ASTM D785 | |
Ball Indentation Hardness (H 961/30)
|
99.0
|
MPa
|
ISO 2039-1 |
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm)
|
109
|
°C
|
ASTM D648 |
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
106
|
°C
|
ISO 75-2/A |
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)
|
120
|
°C
|
ASTM D648 |
Heat Deflection Temperature (1.8 MPa, Annealed)
|
118
|
°C
|
ISO 75-2/A |
Vicat Softening Temperature
|
129
|
°C
|
ASTM D1525 5 |
Vicat Softening Temperature
|
|||
--
|
129
|
°C
|
ISO 306/A50 |
--
|
131
|
°C
|
ISO 306/A120 |
--
|
119
|
°C
|
ISO 306/B50 |
--
|
121
|
°C
|
ISO 306/B120 |
RTI Elec
|
UL 746 | ||
1.50 mm
|
50.0
|
°C
|
|
3.00 mm
|
50.0
|
°C
|
|
RTI Imp
|
UL 746 | ||
1.50 mm
|
50.0
|
°C
|
|
3.00 mm
|
50.0
|
°C
|
|
RTI Str
|
UL 746 | ||
1.50 mm
|
50.0
|
°C
|
|
3.00 mm
|
50.0
|
°C
|
|
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Arc Resistance
|
PLC 6
|
ASTM D495 | |
Comparative Tracking Index (CTI)
|
PLC 0
|
UL 746 | |
High Amp Arc Ignition (HAI)
|
UL 746 | ||
1.50 mm
|
PLC 0
|
||
3.00 mm
|
PLC 0
|
||
High Voltage Arc Tracking Rate (HVTR)
|
PLC 1
|
UL 746 | |
Hot-wire Ignition (HWI)
|
UL 746 | ||
1.50 mm
|
PLC 4
|
||
3.00 mm
|
PLC 4
|
||
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Flame Rating
|
UL 94 | ||
1.50 mm, ALL
|
HB
|
||
1.59 mm
|
HB
|
||
3.00 mm, ALL
|
HB
|