Physical |
Nominal Value
|
Unit
|
Test Method
|
Specific Gravity
|
0.968
|
g/cm³
|
ASTM D792 |
Density
|
0.970
|
g/cm³
|
ISO 1183 |
Outdoor Suitability
|
f1
|
UL 746C | |
Detergent Resistance
|
f4
|
UL 2157 | |
Detergent Resistance
|
f3
|
UL 749 | |
Elastomers |
Nominal Value
|
Unit
|
Test Method
|
Tensile Stress - Across Flow (100% Strain, 23°C)
|
3.60
|
MPa
|
ASTM D412 |
Tensile Stress - Across Flow (100% Strain, 23°C)
|
3.60
|
MPa
|
ISO 37 |
Tensile Strength - Across Flow (Break, 23°C)
|
8.80
|
MPa
|
ASTM D412 |
Tensile Stress - Across Flow (Break, 23°C)
|
8.80
|
MPa
|
ISO 37 |
Tensile Elongation - Across Flow (Break, 23°C)
|
490
|
%
|
ASTM D412 |
Tensile Elongation - Across Flow (Break, 23°C)
|
490
|
%
|
ISO 37 |
Tear Strength - Across Flow 2 (23°C)
|
27.0
|
kN/m
|
ASTM D624 |
Tear Strength - Across Flow 3 (23°C)
|
27
|
kN/m
|
ISO 34-1 |
Compression Set 4
|
ASTM D395B | ||
70°C, 22.0 hr
|
28
|
%
|
|
125°C, 70.0 hr
|
37
|
%
|
|
Compression Set 5
|
ISO 815 | ||
70°C, 22.0 hr
|
28
|
%
|
|
125°C, 70.0 hr
|
37
|
%
|
|
Hardness |
Nominal Value
|
Unit
|
Test Method
|
Shore Hardness (Shore A, 15 sec, 23°C, 2.00 mm)
|
78
|
ISO 868 | |
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Brittleness Temperature
|
-60.0
|
°C
|
ASTM D746 |
Brittleness Temperature
|
-60.0
|
°C
|
ISO 812 |
RTI Elec
|
90.0
|
°C
|
UL 746 |
RTI Str
|
UL 746 | ||
1.00 mm
|
90.0
|
°C
|
|
1.50 mm
|
90.0
|
°C
|
|
3.00 mm
|
95.0
|
°C
|
美国山都坪TPV 101-73 硫化弹性体