| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Density |
1.46
|
--
|
g/cm³
|
ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
|
Across Flow: 2.00 mm
|
1.0
|
--
|
%
|
|
|
Flow: 2.00 mm
|
0.30
|
--
|
%
|
|
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Tensile Modulus (23°C) |
10700
|
11300
|
MPa
|
ISO 527-2 |
| Tensile Stress (Break, 23°C) |
145
|
135
|
MPa
|
ISO 527-2 |
| Tensile Strain (Break, 23°C) |
2.1
|
1.9
|
%
|
ISO 527-2 |
| Flexural Modulus (23°C) |
9800
|
10800
|
MPa
|
ISO 178 |
| Flexural Strength (23°C) |
225
|
200
|
MPa
|
ISO 178 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
|
-30°C
|
7.0
|
7.0
|
kJ/m²
|
|
|
23°C
|
7.0
|
7.0
|
kJ/m²
|
|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
|
-30°C
|
40
|
35
|
kJ/m²
|
|
|
23°C
|
45
|
40
|
kJ/m²
|
|
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Heat Deflection Temperature (1.8 MPa, Unannealed) |
281
|
--
|
°C
|
ISO 75-2/A |
| Melting Temperature 2 |
310
|
--
|
°C
|
ISO 11357-3 |
| CLTE - Flow | ISO 11359-2 | |||
|
-40 to 23°C
|
0.000018
|
--
|
cm/cm/°C
|
|
|
23 to 55°C
|
0.000018
|
--
|
cm/cm/°C
|
|
|
55 to 160°C
|
0.000012
|
--
|
cm/cm/°C
|
|
|
160 to 250°C
|
0.000011
|
--
|
cm/cm/°C
|
|
| CLTE - Transverse | ISO 11359-2 | |||
|
-40 to 23°C
|
0.000060
|
--
|
cm/cm/°C
|
|
|
23 to 55°C
|
0.000062
|
--
|
cm/cm/°C
|
|
|
55 to 160°C
|
0.000095
|
--
|
cm/cm/°C
|
|
|
160 to 250°C
|
0.00012
|
--
|
cm/cm/°C
|
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Comparative Tracking Index |
600
|
--
|
V
|
IEC 60112 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Flame Rating - UL | UL 94 | |||
|
0.400 mm
|
V-0
|
--
|
||
|
3.00 mm
|
V-0
|
--
|
||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
|
0.400 mm
|
960
|
--
|
°C
|
|
|
3.00 mm
|
960
|
--
|
°C
|
|
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
|
0.400 mm
|
700
|
--
|
°C
|
|
|
3.00 mm
|
775
|
--
|
°C
|
|
| UL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| RTI Str | UL 746 | |||
|
0.750 mm
|
125
|
--
|
°C
|
|
|
3.00 mm
|
130
|
--
|
°C
|
|
| RTI Imp | UL 746 | |||
|
0.750 mm
|
115
|
--
|
°C
|
|
|
3.00 mm
|
120
|
--
|
°C
|
|
| RTI Elec | UL 746 | |||
|
0.400 mm
|
140
|
--
|
°C
|
|
|
3.00 mm
|
140
|
--
|
°C
|
HTNFR52G30NHF 无卤阻燃UL94V0 高润滑尼龙