| Physical |
Nominal Value
|
Unit
|
Test Method
|
| Density |
1.68
|
g/cm³
|
ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
|
Across Flow: 2.00 mm
|
0.80
|
%
|
|
|
Flow: 2.00 mm
|
0.20
|
%
|
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
| Tensile Modulus | ISO 527-2 | ||
|
-40°C
|
12000
|
MPa
|
|
|
23°C
|
11300
|
MPa
|
|
|
90°C
|
5900
|
MPa
|
|
|
150°C
|
3650
|
MPa
|
|
| Tensile Stress | ISO 527-2 | ||
|
Break, -40°C
|
172
|
MPa
|
|
|
Break, 23°C
|
130
|
MPa
|
|
|
Break, 90°C
|
67.0
|
MPa
|
|
|
Break, 150°C
|
43.0
|
MPa
|
|
| Tensile Strain | ISO 527-2 | ||
|
Break, -40°C
|
1.8
|
%
|
|
|
Break, 23°C
|
1.9
|
%
|
|
|
Break, 90°C
|
3.5
|
%
|
|
|
Break, 150°C
|
4.0
|
%
|
|
| Flexural Modulus | ISO 178 | ||
|
-40°C
|
11000
|
MPa
|
|
|
23°C
|
10500
|
MPa
|
|
|
90°C
|
4650
|
MPa
|
|
|
150°C
|
2650
|
MPa
|
|
| Flexural Strength | ISO 178 | ||
|
150°C
|
69.0
|
MPa
|
|
|
90°C
|
107
|
MPa
|
|
|
23°C
|
200
|
MPa
|
|
|
-40°C
|
262
|
MPa
|
|
| Impact |
Nominal Value
|
Unit
|
Test Method
|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
|
-40°C
|
8.0
|
kJ/m²
|
|
|
-30°C
|
8.0
|
kJ/m²
|
|
|
23°C
|
9.0
|
kJ/m²
|
|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
|
-40°C
|
30
|
kJ/m²
|
|
|
-30°C
|
35
|
kJ/m²
|
|
|
23°C
|
40
|
kJ/m²
|
|
| Notched Izod Impact Strength | ISO 180/1A | ||
|
-40°C
|
8.0
|
kJ/m²
|
|
|
-30°C
|
8.0
|
kJ/m²
|
|
|
23°C
|
8.5
|
kJ/m²
|
|
| Unnotched Izod Impact Strength | ISO 180/1U | ||
|
-40°C
|
34
|
kJ/m²
|
|
|
-30°C
|
35
|
kJ/m²
|
|
|
23°C
|
40
|
kJ/m²
|
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
| Heat Deflection Temperature (0.45 MPa, Unannealed) |
243
|
°C
|
ISO 75-2/B |
| Heat Deflection Temperature (1.8 MPa, Unannealed) |
220
|
°C
|
ISO 75-2/A |
| Melting Temperature 2 |
252
|
°C
|
ISO 11357-3 |
| CLTE - Flow | ISO 11359-2 | ||
|
-40 to 23°C
|
0.000020
|
cm/cm/°C
|
|
|
23 to 55°C
|
0.000014
|
cm/cm/°C
|
|
|
55 to 160°C
|
4.0E-6
|
cm/cm/°C
|
|
| CLTE - Transverse | ISO 11359-2 | ||
|
-40 to 23°C
|
0.000073
|
cm/cm/°C
|
|
|
23 to 55°C
|
0.000090
|
cm/cm/°C
|
|
|
55 to 160°C
|
0.00012
|
cm/cm/°C
|
|
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
| Flame Rating - UL | UL 94 | ||
|
0.350 mm
|
V-0
|
||
|
0.750 mm
|
V-0
|
||
|
1.50 mm
|
|
||
|
2.00 mm
|
|
||
|
3.00 mm
|
|
||
| Flammability Classification | IEC 60695-11-10, -20 | ||
|
0.350 mm
|
V-0
|
||
|
0.750 mm
|
V-0
|
||
|
1.50 mm
|
|
||
|
2.00 mm
|
|
||
|
3.00 mm
|
|
FR530 美国杜邦PET 加纤30%、防火V0