Physical |
Nominal Value
|
Unit
|
Test Method
|
Density
|
1.56
|
g/cm³
|
ISO 1183 |
Molding Shrinkage
|
ISO 294-4 | ||
Across Flow
|
1.0
|
%
|
|
Flow
|
0.30
|
%
|
|
Water Absorption (Equilibrium, 23°C, 50% RH)
|
1.5
|
%
|
ISO 62 |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Modulus
|
12000
|
MPa
|
ISO 527-2 |
Tensile Stress (Break)
|
170
|
MPa
|
ISO 527-2 |
Tensile Strain (Break)
|
2.0
|
%
|
ISO 527-2 |
Flexural Modulus
|
10000
|
MPa
|
ISO 178 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179/1eA | ||
-30°C
|
8.0
|
kJ/m²
|
|
23°C
|
8.0
|
kJ/m²
|
|
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
290
|
°C
|
ISO 75-2/A |
Melting Temperature 2
|
295
|
°C
|
ISO 11357-3 |
CLTE - Flow
|
0.000020
|
cm/cm/°C
|
ISO 11359-2 |
CLTE - Transverse
|
0.000080
|
cm/cm/°C
|
ISO 11359-2 |
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Volume Resistivity
|
> 1.0E+15
|
ohm·cm
|
IEC 60093 |
Electric Strength
|
30
|
kV/mm
|
IEC 60243-1 |
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Flammability Classification
|
IEC 60695-11-10, -20 | ||
0.750 mm
|
V-0
|
||
1.50 mm
|
V-0
|
TS256F6 荷兰DSM PA46 防火V0 英文物性