Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Density
|
1.18
|
--
|
g/cm³
|
ISO 1183 |
Molding Shrinkage
|
ISO 294-4 | |||
Across Flow
|
2.0
|
--
|
%
|
|
Flow
|
2.0
|
--
|
%
|
|
Water Absorption (Equilibrium, 23°C, 50% RH)
|
3.7
|
--
|
%
|
ISO 62 |
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus
|
ISO 527-2 | |||
--
|
3300
|
1000
|
MPa
|
|
120°C
|
800
|
--
|
MPa
|
|
160°C
|
650
|
--
|
MPa
|
|
180°C
|
600
|
--
|
MPa
|
|
200°C
|
500
|
--
|
MPa
|
|
Tensile Stress
|
ISO 527-2 | |||
Yield
|
100
|
55.0
|
MPa
|
|
Yield, 120°C
|
50.0
|
--
|
MPa
|
|
Yield, 160°C
|
40.0
|
--
|
MPa
|
|
Yield, 180°C
|
35.0
|
--
|
MPa
|
|
Yield, 200°C
|
30.0
|
--
|
MPa
|
|
Nominal Tensile Strain at Break
|
ISO 527-2 | |||
--
|
40
|
> 50
|
%
|
|
120°C
|
> 50
|
--
|
%
|
|
160°C
|
> 50
|
--
|
%
|
|
180°C
|
> 50
|
--
|
%
|
|
200°C
|
> 50
|
--
|
%
|
|
Flexural Modulus
|
ISO 178 | |||
--
|
3000
|
900
|
MPa
|
|
120°C
|
800
|
--
|
MPa
|
|
160°C
|
600
|
--
|
MPa
|
|
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
-30°C
|
4.0
|
4.0
|
kJ/m²
|
|
23°C
|
10
|
35
|
kJ/m²
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
-30°C
|
No Break
|
No Break
|
||
23°C
|
No Break
|
No Break
|
||
Notched Izod Impact Strength
|
ISO 180/1A | |||
-40°C
|
4.0
|
4.0
|
kJ/m²
|
|
23°C
|
10
|
35
|
kJ/m²
|
|
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
190
|
--
|
°C
|
ISO 75-2/A |
Melting Temperature 2
|
295
|
--
|
°C
|
ISO 11357-3 |
CLTE - Flow
|
0.000085
|
--
|
cm/cm/°C
|
ISO 11359-2 |
CLTE - Transverse
|
0.00011
|
--
|
cm/cm/°C
|
ISO 11359-2 |
Thermal Index - 5000 hr
|
152
|
--
|
°C
|
IEC 60216 |
Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Volume Resistivity
|
1.0E+15
|
1.0E+9
|
ohm·cm
|
IEC 60093 |
Electric Strength
|
25
|
15
|
kV/mm
|
IEC 60243-1 |
Comparative Tracking Index
|
400
|
--
|
V
|
IEC 60112 |
Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flammability Classification
|
IEC 60695-11-10, -20 | |||
0.750 mm
|
V-2
|
--
|
||
1.50 mm
|
V-2
|
--
|
PA46 荷兰DSM TW300 热稳定 英文物性