| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.62
|
g/cm³
|
ISO 1183 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
13000
|
MPa
|
ISO 527-2/1A/1 |
|
Tensile Stress (Break)
|
130
|
MPa
|
ISO 527-2/1A/5 |
|
Tensile Strain (Break)
|
1.8
|
%
|
ISO 527-2/1A/5 |
|
Flexural Modulus (23°C)
|
12000
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (23°C)
|
35
|
kJ/m²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength (23°C)
|
35
|
kJ/m²
|
ISO 179/1eU |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
265
|
°C
|
ISO 75-2/A |
|
Melting Temperature 2
|
335
|
°C
|
ISO 11357-3 |
|
CLTE - Flow
|
3.0E-6
|
cm/cm/°C
|
ISO 11359-2 |
|
CLTE - Transverse
|
0.000070
|
cm/cm/°C
|
ISO 11359-2 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
> 1.0E+16
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
> 1.0E+16
|
ohm·cm
|
IEC 60093 |
|
Electric Strength
|
36
|
kV/mm
|
IEC 60243-1 |
|
Relative Permittivity (1 MHz)
|
4.00
|
IEC 60250 | |
|
Dissipation Factor (1 MHz)
|
0.031
|
IEC 60250 | |
|
Comparative Tracking Index
|
200
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
0.380 mm
|
V-0
|
||
|
1.50 mm
|
V-0
|
美国杜邦LCP 6130L 加纤30% 英文物性