| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.14
|
--
|
g/cm³
|
ASTM D792 |
|
Density
|
1.14
|
--
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage - Flow
|
1.3 to 2.0
|
--
|
%
|
Internal Method |
|
Water Absorption (Equilibrium)
|
--
|
2.5
|
%
|
ASTM D570 |
|
Water Absorption (Equilibrium, 23°C, 50% RH)
|
--
|
2.5
|
%
|
ISO 62 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
3000
|
1200
|
MPa
|
ISO 527-2 |
|
Tensile Strength
|
79.0
|
57.0
|
MPa
|
ASTM D638 |
|
Tensile Stress (Yield, 23°C)
|
82.0
|
52.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Yield, 23°C)
|
4.0
|
24
|
%
|
ISO 527-2 |
|
Tensile Elongation (Break)
|
50
|
250
|
%
|
ASTM D638 |
|
Tensile Strain (Break, 23°C)
|
--
|
> 100
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
2800
|
1200
|
MPa
|
ASTM D790 |
|
Flexural Modulus (23°C)
|
2700
|
1100
|
MPa
|
ISO 178 |
|
Flexural Strength
|
118
|
54.0
|
MPa
|
ASTM D790 |
|
Flexural Strength (23°C)
|
113
|
42.0
|
MPa
|
ISO 178 |
|
Taber Abrasion Resistance
|
--
|
7.00
|
mg
|
ASTM D1044 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
6.0
|
15
|
kJ/m²
|
ISO 179 |
|
Charpy Unnotched Impact Strength
|
No Break
|
No Break
|
ISO 179 | |
|
Notched Izod Impact
|
39
|
150
|
J/m
|
ASTM D256 |
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Rockwell Hardness
|
ASTM D785 | |||
|
M-Scale
|
80
|
55
|
||
|
R-Scale
|
120
|
108
|
||
|
Rockwell Hardness
|
ISO 2039-2 | |||
|
M-Scale
|
80
|
55
|
||
|
R-Scale
|
120
|
108
|
||
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (0.45 MPa, Unannealed)
|
230
|
--
|
°C
|
ASTM D648 |
|
Heat Deflection Temperature (0.45 MPa, Unannealed)
|
192
|
--
|
°C
|
ISO 75-2/B |
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
70.0
|
--
|
°C
|
ASTM D648 |
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
68.0
|
--
|
°C
|
ISO 75-2/A |
|
CLTE - Flow
|
0.000080
|
--
|
cm/cm/°C
|
ASTM D696 |
|
CLTE - Flow
|
0.000080
|
--
|
cm/cm/°C
|
ISO 11359-2 |
|
Specific Heat
|
1670
|
--
|
J/kg/°C
|
|
|
Thermal Conductivity
|
0.20
|
--
|
W/m/K
|
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+13
|
--
|
ohm
|
IEC 60093 |
|
Volume Resistivity (23°C)
|
1.0E+14
|
--
|
ohm·cm
|
IEC 60093 |
|
Electric Strength
|
20
|
--
|
kV/mm
|
IEC 60243-1 |
|
Comparative Tracking Index (3.00 mm)
|
600
|
--
|
V
|
IEC 60112 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | |||
|
0.794 mm
|
V-2
|
--
|
||
|
1.59 mm
|
V-2
|
--
|
| Processing Information |