| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density
|
1.37
|
--
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage
|
Internal Method | |||
|
Across Flow: 3.00 mm
|
0.60 to 0.90
|
--
|
%
|
|
|
Flow: 3.00 mm
|
0.20 to 0.50
|
--
|
%
|
|
|
Water Absorption (23°C, 24 hr)
|
0.60
|
--
|
%
|
ISO 62 |
|
Water Absorption (Saturation, 23°C)
|
5.5
|
--
|
%
|
ISO 62 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Stress
|
ISO 527-2 | |||
|
Yield, -40°C
|
235
|
215
|
MPa
|
|
|
Yield, 23°C
|
190
|
140
|
MPa
|
|
|
Yield, 80°C
|
120
|
100
|
MPa
|
|
|
Tensile Strain
|
ISO 527-2 | |||
|
Break, -40°C
|
2.0
|
2.5
|
%
|
|
|
Break, 23°C
|
2.5
|
3.0
|
%
|
|
|
Break, 80°C
|
5.0
|
5.5
|
%
|
|
|
Flexural Modulus
|
ISO 178 | |||
|
-40°C
|
11600
|
10500
|
MPa
|
|
|
23°C
|
9500
|
6800
|
MPa
|
|
|
80°C
|
5800
|
4300
|
MPa
|
|
|
Flexural Strength
|
ISO 178 | |||
|
80°C
|
190
|
135
|
MPa
|
|
|
23°C
|
290
|
215
|
MPa
|
|
|
-40°C
|
325
|
315
|
MPa
|
|
|
Compressive Stress
|
ISO 604 | |||
|
-40°C
|
250
|
200
|
MPa
|
|
|
23°C
|
180
|
110
|
MPa
|
|
|
80°C
|
110
|
70.0
|
MPa
|
|
|
Shear Strength (23°C)
|
95.0
|
85.0
|
MPa
|
ASTM D732 |
|
Coefficient of Friction
|
||||
|
-- 2
|
< 0.15
|
--
|
||
|
-- 3
|
0.40
|
--
|
||
|
Taber Abrasion Resistance (1000 Cycles)
|
24.0
|
--
|
mg
|
|
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179 | |||
|
-40°C
|
10
|
12
|
kJ/m²
|
|
|
23°C
|
13
|
16
|
kJ/m²
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179 | |||
|
-40°C
|
60
|
70
|
kJ/m²
|
|
|
23°C
|
65
|
75
|
kJ/m²
|
|
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Rockwell Hardness
|
ISO 2039-2 | |||
|
M-Scale, 23°C
|
97
|
--
|
||
|
R-Scale, 23°C
|
121
|
--
|
||
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Heat Deflection Temperature (0.45 MPa, Unannealed)
|
262
|
--
|
°C
|
ISO 75-2/B |
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
255
|
--
|
°C
|
ISO 75-2/A |
|
Melting Temperature
|
265
|
--
|
°C
|
DSC |
|
CLTE - Flow
|
0.000020 to 0.000030
|
--
|
cm/cm/°C
|
ISO 11359-2 |
|
Specific Heat
|
1800
|
--
|
J/kg/°C
|
|
|
Thermal Conductivity
|
0.40
|
--
|
W/m/K
|
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Volume Resistivity
|
1.0E+15
|
1.0E+12 to 1.0E+13
|
ohm·cm
|
IEC 60093 |
|
Electric Strength (3.00 mm)
|
20
|
17
|
kV/mm
|
IEC 60243-1 |
|
Dielectric Constant 4
|
IEC 60250 | |||
|
23°C, 50 Hz
|
4.60
|
6.30
|
||
|
23°C, 1 kHz
|
4.40
|
5.50
|
||
|
23°C, 1 MHz
|
3.90
|
4.00
|
||
|
Dissipation Factor 4
|
IEC 60250 | |||
|
23°C, 50 Hz
|
0.020
|
0.080
|
||
|
23°C, 1 kHz
|
0.020
|
0.080
|
||
|
23°C, 1 MHz
|
0.020
|
0.040
|
||
|
Arc Resistance 5
|
114
|
120
|
sec
|
UL 746 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Flame Rating (0.794 mm)
|
HB
|
--
|
UL 94 |
日本东丽PA66 CM3001G-33 英文物性表