| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density
|
1.14
|
--
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage
|
Internal Method | |||
|
1.00 mm
|
0.80 to 1.5
|
--
|
%
|
|
|
3.00 mm
|
1.5 to 2.2
|
--
|
%
|
|
|
Water Absorption (23°C, 24 hr)
|
1.2
|
--
|
%
|
ISO 62 |
|
Water Absorption (Saturation, 23°C)
|
8.0
|
--
|
%
|
ISO 62 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Stress
|
ISO 527-2 | |||
|
Yield, -40°C
|
115
|
110
|
MPa
|
|
|
Yield, 23°C
|
80.0
|
50.0
|
MPa
|
|
|
Yield, 80°C
|
40.0
|
40.0
|
MPa
|
|
|
Tensile Strain (Yield, 23°C)
|
1.5
|
--
|
%
|
ISO 527-2 |
|
Tensile Strain (Break, 23°C)
|
25
|
> 50
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
ISO 178 | |||
|
-40°C
|
4300
|
4100
|
MPa
|
|
|
23°C
|
2800
|
1400
|
MPa
|
|
|
80°C
|
900
|
500
|
MPa
|
|
|
Flexural Strength
|
ISO 178 | |||
|
80°C
|
65.0
|
40.0
|
MPa
|
|
|
23°C
|
115
|
65.0
|
MPa
|
|
|
-40°C
|
140
|
125
|
MPa
|
|
|
Compressive Stress (23°C)
|
90.0
|
--
|
MPa
|
ISO 604 |
|
Shear Strength (23°C)
|
80.0
|
75.0
|
MPa
|
ASTM D732 |
|
Coefficient of Friction 2
|
0.15 to 0.20
|
--
|
||
|
Taber Abrasion Resistance (1000 Cycles)
|
8.00
|
--
|
mg
|
|
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179 | |||
|
-40°C
|
2.5
|
--
|
kJ/m²
|
|
|
23°C
|
4.0
|
24
|
kJ/m²
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179 | |||
|
-40°C
|
No Break
|
--
|
||
|
23°C
|
No Break
|
--
|
||
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Rockwell Hardness
|
ISO 2039-2 | |||
|
R-Scale, 80°C
|
97
|
--
|
||
|
R-Scale, 23°C
|
119
|
100
|
||
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Heat Deflection Temperature (0.45 MPa, Unannealed)
|
220
|
--
|
°C
|
ISO 75-2/B |
|
Melting Temperature
|
265
|
--
|
°C
|
DSC |
|
CLTE - Flow
|
0.000090 to 0.00010
|
--
|
cm/cm/°C
|
ISO 11359-2 |
|
Specific Heat
|
2100
|
--
|
J/kg/°C
|
|
|
Thermal Conductivity
|
0.32
|
--
|
W/m/K
|
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Volume Resistivity
|
1.0E+14 to 1.0E+15
|
1.0E+12 to 1.0E+13
|
ohm·cm
|
IEC 60093 |
|
Electric Strength (3.00 mm)
|
18
|
--
|
kV/mm
|
IEC 60243-1 |
|
Dielectric Constant 3
|
IEC 60250 | |||
|
23°C, 50 Hz
|
4.00
|
7.50
|
||
|
23°C, 1 kHz
|
3.90
|
6.50
|
||
|
23°C, 1 MHz
|
3.30
|
3.80
|
||
|
Dissipation Factor 3
|
IEC 60250 | |||
|
23°C, 50 Hz
|
0.030
|
0.060
|
||
|
23°C, 1 kHz
|
0.030
|
0.060
|
||
|
23°C, 1 MHz
|
0.020
|
0.070
|
||
|
Arc Resistance 4
|
130
|
--
|
sec
|
UL 746 |
|
Comparative Tracking Index (CTI)
|
> 600
|
--
|
V
|
UL 746 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Flame Rating (0.397 mm)
|
V-2
|
--
|
UL 94 |
日本东丽PA66 CM3001-N英文物性表 价格