Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Specific Gravity
|
1.34
|
--
|
g/cm³
|
ASTM D792 |
Density
|
1340
|
--
|
kg/m³
|
ISO 1183 2 |
Melt volume-flow rate (275°C/5.0 kg)
|
40.0
|
--
|
cm³/10min
|
ISO 1133 2 |
Molding Shrinkage - Flow (3.18 mm)
|
0.50
|
--
|
%
|
ASTM D955 |
Water Absorption (Saturation)
|
6.0
|
--
|
%
|
ASTM D570 |
Water Absorption (Saturation)
|
6.0
|
--
|
%
|
ISO 62 2 |
Water Absorption (Equilibrium, 50% RH)
|
1.4
|
--
|
%
|
ASTM D570 |
Water Absorption (Equilibrium)
|
1.4
|
--
|
%
|
ISO 62 2 |
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile modulus
|
8500
|
6000
|
MPa
|
ISO 527-2 2 |
Tensile Strength (Break, 23°C)
|
138
|
--
|
MPa
|
ASTM D638 |
Tensile Stress (Break, -40°C)
|
196
|
--
|
MPa
|
ISO 527-2 |
Tensile Stress (Break)
|
140
|
100
|
MPa
|
ISO 527-2 2 |
Tensile Elongation (Break, 23°C)
|
3.0
|
--
|
%
|
ASTM D638 |
Tensile Strain (Break)
|
3.0
|
4.5
|
%
|
ISO 527-2 2 |
Flexural Modulus (23°C)
|
7100
|
--
|
MPa
|
ASTM D790 |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy notched impact strength (23°C)
|
13.0
|
17.0
|
kJ/m²
|
ISO 179/1eA 2 |
Charpy notched impact strength (-30°C)
|
10.0
|
--
|
kJ/m²
|
ISO 179/1eA 2 |
Charpy impact strength (23°C)
|
65.0
|
70.0
|
kJ/m²
|
ISO 179/1eU 2 |
Charpy impact strength (-30°C)
|
60.0
|
65.0
|
kJ/m²
|
ISO 179/1eU 2 |
Notched Izod Impact
|
ASTM D256 | |||
-40°C
|
64
|
--
|
J/m
|
|
23°C
|
75
|
--
|
J/m
|
|
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Deflection Temperature Under Load (0.45 MPa, Unannealed)
|
250
|
--
|
°C
|
ASTM D648 |
Deflection Temperature Under Load (0.45 MPa)
|
250
|
--
|
°C
|
ISO 75-2 2 |
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
238
|
--
|
°C
|
ASTM D648 |
Deflection Temperature Under Load (1.8 MPa)
|
250
|
--
|
°C
|
ISO 75-2 2 |
Peak Melting Temperature
|
260
|
--
|
°C
|
ASTM D3418 |
Melting Temperature (DSC)
|
260
|
--
|
°C
|
ISO 3146 |
CLTE - Flow
|
0.000020
|
--
|
cm/cm/°C
|
ASTM E831 |
CLTE - Flow
|
0.000030
|
--
|
cm/cm/°C
|
ISO 11359-2 |
CLTE - Transverse
|
0.000070
|
--
|
cm/cm/°C
|
ISO 11359-2 |
RTI Elec (1.50 mm)
|
120
|
--
|
°C
|
UL 746 |
RTI Imp (1.50 mm)
|
115
|
--
|
°C
|
UL 746 |
RTI Str (1.50 mm)
|
130
|
--
|
°C
|
UL 746 |
Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Volume Resistivity (1.50 mm)
|
1.0E+13
|
1.0E+10
|
ohm·cm
|
ASTM D257 |
Volume resistivity
|
1.0E+11
|
1.0E+8
|
ohm·m
|
IEC 60093 2 |
Electric strength
|
33
|
30
|
kV/mm
|
IEC 60243-1 2 |
Relative Permittivity (1 MHz)
|
3.70
|
5.00
|
IEC 60250 2 | |
Dissipation Factor (1 MHz)
|
0.020
|
0.10
|
IEC 60250 2 | |
Comparative tracking index
|
550
|
550
|
IEC 60112 2 | |
Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flame Rating (1.50 mm)
|
V-0
|
--
|
UL 94 |
PA66 A3X2G5 德国巴斯夫 A3X2G5英文物性