| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.36
|
--
|
g/cm³
|
ASTM D792 |
|
Density
|
1360
|
--
|
kg/m³
|
ISO 1183 2 |
|
Melt volume-flow rate (275°C/5.0 kg)
|
40.0
|
--
|
cm³/10min
|
ISO 1133 2 |
|
Molding Shrinkage - Flow (3.18 mm)
|
0.30
|
--
|
%
|
ASTM D955 |
|
Water Absorption (Saturation)
|
5.5
|
--
|
%
|
ASTM D570 |
|
Water Absorption (Saturation)
|
5.5
|
--
|
%
|
ISO 62 2 |
|
Water Absorption (Equilibrium, 50% RH)
|
1.7
|
--
|
%
|
ASTM D570 |
|
Water Absorption (Equilibrium)
|
1.7
|
--
|
%
|
ISO 62 2 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile modulus
|
10000
|
7200
|
MPa
|
ISO 527-2 2 |
|
Tensile Strength (Break, 23°C)
|
186
|
--
|
MPa
|
ASTM D638 |
|
Tensile Stress (Break, -40°C)
|
238
|
227
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break)
|
190
|
130
|
MPa
|
ISO 527-2 2 |
|
Tensile Elongation (Break, 23°C)
|
3.0
|
--
|
%
|
ASTM D638 |
|
Tensile Strain (Break)
|
3.0
|
5.0
|
%
|
ISO 527-2 2 |
|
Flexural Modulus (23°C)
|
8600
|
6500
|
MPa
|
ISO 178 |
|
Flexural Strength (23°C)
|
280
|
210
|
MPa
|
ISO 178 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy notched impact strength (23°C)
|
13.0
|
22.0
|
kJ/m²
|
ISO 179/1eA 2 |
|
Charpy notched impact strength (-30°C)
|
11.0
|
--
|
kJ/m²
|
ISO 179/1eA 2 |
|
Charpy impact strength (23°C)
|
85.0
|
100
|
kJ/m²
|
ISO 179/1eU 2 |
|
Charpy impact strength (-30°C)
|
70.0
|
--
|
kJ/m²
|
ISO 179/1eU 2 |
|
Notched Izod Impact
|
ASTM D256 | |||
|
-40°C
|
91
|
--
|
J/m
|
|
|
23°C
|
110
|
--
|
J/m
|
|
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (0.45 MPa, Unannealed)
|
250
|
--
|
°C
|
ASTM D648 |
|
Deflection Temperature Under Load (0.45 MPa)
|
250
|
--
|
°C
|
ISO 75-2 2 |
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
250
|
--
|
°C
|
ASTM D648 |
|
Deflection Temperature Under Load (1.8 MPa)
|
250
|
--
|
°C
|
ISO 75-2 2 |
|
Peak Melting Temperature
|
260
|
--
|
°C
|
ASTM D3418 |
|
Melting Temperature (DSC)
|
260
|
--
|
°C
|
ISO 3146 |
|
CLTE - Flow
|
0.000010
|
--
|
cm/cm/°C
|
ASTM E831 |
|
CLTE - Flow
|
0.000025
|
--
|
cm/cm/°C
|
ISO 11359-2 |
|
CLTE - Transverse
|
0.000065
|
--
|
cm/cm/°C
|
ISO 11359-2 |
|
RTI Elec (1.50 mm)
|
120
|
--
|
°C
|
UL 746 |
|
RTI Imp (1.50 mm)
|
120
|
--
|
°C
|
UL 746 |
|
RTI Str (1.50 mm)
|
130
|
--
|
°C
|
UL 746 |
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Volume Resistivity (1.50 mm)
|
1.0E+13
|
1.0E+10
|
ohm·cm
|
ASTM D257 |
|
Volume resistivity
|
1.0E+11
|
1.0E+8
|
ohm·m
|
IEC 60093 2 |
|
Relative Permittivity (100 Hz)
|
--
|
5.60
|
IEC 60250 2 | |
|
Relative Permittivity (1 MHz)
|
3.50
|
--
|
IEC 60250 2 | |
|
Dissipation Factor (100 Hz)
|
0.014
|
0.23
|
IEC 60250 2 | |
|
Dissipation Factor (1 MHz)
|
0.014
|
0.16
|
IEC 60250 2 | |
|
Comparative tracking index
|
550
|
550
|
IEC 60112 2 | |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Flame Rating (1.50 mm)
|
HB
|
--
|
UL 94 |