点击图片查看原图
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density
|
1.56
|
--
|
g/cm³
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)
|
20.0
|
--
|
cm³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
0.45
|
--
|
%
|
ISO 294-4 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
16800
|
12500
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break, 23°C)
|
240
|
180
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break, 23°C)
|
2.5
|
3.5
|
%
|
ISO 527-2 |
|
Tensile Creep Modulus (1000 hr)
|
--
|
7800
|
MPa
|
ISO 899-1 |
|
Flexural Modulus (23°C)
|
15000
|
13500
|
MPa
|
ISO 178 |
|
Flexural Strength (23°C)
|
360
|
300
|
MPa
|
ISO 178 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
13
|
--
|
kJ/m²
|
|
|
23°C
|
18
|
25
|
kJ/m²
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
|
-30°C
|
90
|
--
|
kJ/m²
|
|
|
23°C
|
95
|
100
|
kJ/m²
|
|
|
Notched Izod Impact Strength (23°C)
|
13
|
15
|
kJ/m²
|
ISO 180/1A |
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Heat Deflection Temperature (0.45 MPa, Unannealed)
|
250
|
--
|
°C
|
ISO 75-2/B |
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
250
|
--
|
°C
|
ISO 75-2/A |
|
Melting Temperature (DSC)
|
260
|
--
|
°C
|
ISO 3146 |
|
CLTE - Flow (23 to 80°C)
|
5.0E-6 to 0.000020
|
--
|
cm/cm/°C
|
ISO 11359-2 |
|
CLTE - Transverse (23 to 80°C)
|
0.000050 to 0.000060
|
--
|
cm/cm/°C
|
ISO 11359-2 |
|
Thermal Conductivity
|
0.37
|
--
|
W/m/K
|
ISO 8302 |
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Surface Resistivity
|
--
|
1.0E+10
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
1.0E+15
|
1.0E+12
|
ohm·cm
|
IEC 60093 |
|
Relative Permittivity (23°C, 1 MHz)
|
3.80
|
6.60
|
IEC 60250 | |
|
Dissipation Factor (23°C, 1 MHz)
|
0.015
|
0.17
|
IEC 60250 | |
|
Comparative Tracking Index (Solution A)
|
550
|
--
|
V
|
IEC 60112 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Flame Rating (1.60 mm)
|
HB
|
--
|
UL 94 |