Physical |
Nominal Value
|
Unit
|
Test Method
|
Density
|
1.13
|
g/cm³
|
ISO 1183 |
Water Absorption (Saturation, 23°C)
|
8.5
|
%
|
ISO 62 |
Water Absorption (Equilibrium, 23°C, 50% RH)
|
2.8
|
%
|
ISO 62 |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Modulus (23°C)
|
3000
|
MPa
|
ISO 527-2 |
Tensile Stress (Yield, 23°C)
|
85.0
|
MPa
|
ISO 527-2 |
Tensile Strain (Yield, 23°C)
|
5.0
|
%
|
ISO 527-2 |
Nominal Tensile Strain at Break (23°C)
|
20
|
%
|
ISO 527-2 |
Flexural Modulus (23°C)
|
2900
|
MPa
|
ISO 178 |
Flexural Strength (23°C)
|
100
|
MPa
|
ISO 178 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Charpy Notched Impact Strength (23°C)
|
5.0
|
kJ/m²
|
ISO 179 |
Charpy Unnotched Impact Strength
|
ISO 179 | ||
-30°C
|
No Break
|
||
23°C
|
No Break
|
||
Notched Izod Impact Strength (23°C)
|
5.5
|
kJ/m²
|
ISO 180 |
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
75.0
|
°C
|
ISO 75-2/A |
Melting Temperature (DSC)
|
260
|
°C
|
ISO 3146 |
PA66 A3K价格 PA66 A3K英文物性