| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Specific Gravity |
1.38
|
--
|
g/cm³
|
ASTM D792 |
| Density |
1.39
|
--
|
g/cm³
|
ISO 1183 |
| Molding Shrinkage - Flow | Internal Method | |||
|
1.60 mm
|
0.20
|
--
|
%
|
|
|
3.20 mm
|
0.30
|
--
|
%
|
|
|
6.40 mm
|
0.50
|
--
|
%
|
|
| Molding Shrinkage - Across Flow | Internal Method | |||
|
1.60 mm
|
1.0
|
--
|
%
|
|
|
3.20 mm
|
1.0
|
--
|
%
|
|
|
6.40 mm
|
1.1
|
--
|
%
|
|
| Molding Shrinkage | ISO 294-4 | |||
|
Across Flow: 2.00 mm
|
1.1
|
--
|
%
|
|
|
Flow: 2.00 mm
|
0.30
|
--
|
%
|
|
| Water Absorption (23°C, 24 hr) |
0.70
|
--
|
%
|
ASTM D570 |
| Water Absorption (23°C, 24 hr) |
1.2
|
--
|
%
|
ISO 62 |
| Water Absorption (Saturation, 23°C) |
5.4
|
--
|
%
|
ASTM D570 |
| Water Absorption (Saturation, 23°C) |
5.7
|
--
|
%
|
ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) |
1.8
|
--
|
%
|
ISO 62 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Tensile Modulus (23°C) |
10500
|
8000
|
MPa
|
ISO 527-2 |
| Tensile Strength | ASTM D638 | |||
|
-40°C
|
214
|
207
|
MPa
|
|
|
23°C
|
186
|
124
|
MPa
|
|
|
77°C
|
110
|
86.0
|
MPa
|
|
| Tensile Stress (Break, 23°C) |
200
|
140
|
MPa
|
ISO 527-2 |
| Tensile Elongation (Break, 23°C) |
3.0
|
4.0
|
%
|
ASTM D638 |
| Tensile Strain (Break, 23°C) |
3.5
|
5.0
|
%
|
ISO 527-2 |
| Flexural Modulus (23°C) |
8970
|
6210
|
MPa
|
ASTM D790 |
| Flexural Modulus (23°C) |
9300
|
6210
|
MPa
|
ISO 178 |
| Flexural Strength (23°C) |
262
|
--
|
MPa
|
ASTM D790 |
| Flexural Strength (23°C) |
290
|
200
|
MPa
|
ISO 178 |
| Shear Strength (23°C) |
86.0
|
--
|
MPa
|
ASTM D732 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
|
-40°C
|
10
|
10
|
kJ/m²
|
|
|
-30°C
|
10
|
10
|
kJ/m²
|
|
|
23°C
|
13
|
17
|
kJ/m²
|
|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
|
-30°C
|
70
|
75
|
kJ/m²
|
|
|
23°C
|
85
|
100
|
kJ/m²
|
|
| Notched Izod Impact (23°C) |
120
|
130
|
J/m
|
ASTM D256 |
| Notched Izod Impact Strength | ISO 180/1A | |||
|
-40°C
|
10
|
10
|
kJ/m²
|
|
|
-30°C
|
10
|
10
|
kJ/m²
|
|
|
23°C
|
12
|
15
|
kJ/m²
|
|
| Unnotched Izod Impact (23°C) |
1300
|
1500
|
J/m
|
ASTM D4812 |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
|
-30°C
|
70
|
70
|
kJ/m²
|
|
|
23°C
|
80
|
90
|
kJ/m²
|
|
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Rockwell Hardness (M-Scale) |
101
|
--
|
ASTM D785 | |
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) |
261
|
--
|
°C
|
ASTM D648 |
| Heat Deflection Temperature (0.45 MPa, Unannealed) |
261
|
--
|
°C
|
ISO 75-2/B |
| Deflection Temperature Under Load (1.8 MPa, Unannealed) |
249
|
--
|
°C
|
ASTM D648 |
| Heat Deflection Temperature (1.8 MPa, Unannealed) |
252
|
--
|
°C
|
ISO 75-2/A |
| Glass Transition Temperature |
80.0
|
--
|
°C
|
ISO 11357-2 |
| Melting Temperature |
263
|
--
|
°C
|
ASTM D3418 |
| Melting Temperature 2 |
262
|
--
|
°C
|
ISO 11357-3 |
| CLTE - Flow | ASTM E831 | |||
|
-40 to 23°C
|
0.000024
|
--
|
cm/cm/°C
|
|
|
23 to 55°C
|
0.000018
|
--
|
cm/cm/°C
|
|
|
55 to 160°C
|
0.000013
|
--
|
cm/cm/°C
|
|
| CLTE - Flow | ISO 11359-2 | |||
|
-40 to 23°C
|
0.000024
|
--
|
cm/cm/°C
|
|
|
23 to 55°C
|
0.000018
|
--
|
cm/cm/°C
|
|
|
55 to 160°C
|
0.000013
|
--
|
cm/cm/°C
|
|
| CLTE - Transverse | ASTM E831 | |||
|
-40 to 23°C
|
0.000065
|
--
|
cm/cm/°C
|
|
|
23 to 55°C
|
0.000083
|
--
|
cm/cm/°C
|
|
|
55 to 160°C
|
0.00014
|
--
|
cm/cm/°C
|
|
| CLTE - Transverse | ISO 11359-2 | |||
|
-40 to 23°C
|
0.000065
|
--
|
cm/cm/°C
|
|
|
23 to 55°C
|
0.000083
|
--
|
cm/cm/°C
|
|
|
55 to 160°C
|
0.00014
|
--
|
cm/cm/°C
|
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Volume Resistivity (23°C) |
1.0E+15
|
--
|
ohm·cm
|
ASTM D257 |
| Volume Resistivity |
1.0E+15
|
1.0E+11
|
ohm·cm
|
IEC 60093 |
| Dielectric Strength 3 (23°C, 3.20 mm) |
21
|
--
|
kV/mm
|
ASTM D149 |
| Dielectric Constant | ASTM D150 | |||
|
23°C, 1 kHz
|
4.50
|
--
|
||
|
23°C, 1 MHz
|
3.70
|
--
|
||
| Relative Permittivity | IEC 60250 | |||
|
23°C, 100 Hz
|
4.20
|
--
|
||
|
23°C, 1 MHz
|
4.00
|
--
|
||
| Dissipation Factor (23°C, 1 MHz) |
0.020
|
--
|
ASTM D150 | |
| Dissipation Factor | IEC 60250 | |||
|
23°C, 100 Hz
|
0.010
|
--
|
||
|
23°C, 1 MHz
|
0.015
|
--
|
||
| Electric Strength (23°C, 2.00 mm) |
27
|
--
|
kV/mm
|
IEC 60243-1 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Flame Rating - UL | UL 94 | |||
|
0.710 mm
|
HB
|
--
|
||
|
0.750 mm
|
HB
|
--
|
||
|
1.50 mm
|
HB
|
--
|
||
|
3.00 mm
|
HB
|
--
|
||
| Flammability Classification | IEC 60695-11-10, -20 | |||
|
0.710 mm
|
HB
|
--
|
||
|
0.750 mm
|
HB
|
--
|
||
|
1.50 mm
|
HB
|
--
|
||
|
3.00 mm
|
HB
|
--
|
||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
|
0.710 mm
|
725
|
--
|
°C
|
|
|
1.50 mm
|
700
|
--
|
°C
|
|
|
3.00 mm
|
800
|
--
|
°C
|
|
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
|
0.710 mm
|
750
|
--
|
°C
|
|
|
1.50 mm
|
725
|
--
|
°C
|
|
|
3.00 mm
|
825
|
--
|
°C
|
|
| Oxygen Index |
24
|
--
|
%
|
ISO 4589-2 |
| UL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| RTI Str | UL 746 | |||
|
0.710 mm
|
140
|
--
|
°C
|
|
|
1.50 mm
|
140
|
--
|
°C
|
|
|
3.00 mm
|
140
|
--
|
°C
|
|
| RTI Imp | UL 746 | |||
|
0.710 mm
|
125
|
--
|
°C
|
|
|
1.50 mm
|
125
|
--
|
°C
|
|
|
3.00 mm
|
125
|
--
|
°C
|
|
| RTI Elec | UL 746 | |||
|
0.710 mm
|
140
|
--
|
°C
|
|
|
1.50 mm
|
140
|
--
|
°C
|
|
|
3.00 mm
|
140
|
--
|
°C
|
|
| Comparative Tracking Index (CTI) |
408
|
--
|
V
|
UL 746 |
| Comparative Tracking Index (CTI) (PLC) (3.00 mm) |
PLC 1
|
--
|
UL 746 |
PA66 70G33HS1L价格 70G33HS1L英文物性