Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Density |
1.60
|
--
|
g/cm³
|
ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow: 2.00 mm
|
0.80
|
--
|
%
|
|
Flow: 2.00 mm
|
0.30
|
--
|
%
|
|
Water Absorption (Equilibrium, 23°C, 1.00 mm, 50% RH) |
0.70
|
--
|
%
|
ISO 62 |
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus (23°C) |
10600
|
7500
|
MPa
|
ISO 527-2 |
Tensile Stress (Break, 23°C) |
170
|
--
|
MPa
|
ISO 527-2 |
Tensile Strain (Break, 23°C) |
2.5
|
--
|
%
|
ISO 527-2 |
Flexural Modulus (23°C) |
9450
|
--
|
MPa
|
ISO 178 |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength | ISO 179/1eA | |||
-40°C
|
11
|
--
|
kJ/m²
|
|
23°C
|
11
|
--
|
kJ/m²
|
|
Charpy Unnotched Impact Strength (23°C) |
40
|
--
|
kJ/m²
|
ISO 179/1eU |
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Heat Deflection Temperature (1.8 MPa, Unannealed) |
246
|
--
|
°C
|
ISO 75-2/A |
Melting Temperature 2 |
261
|
--
|
°C
|
ISO 11357-3 |
Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Volume Resistivity |
1.0E+16
|
--
|
ohm·cm
|
IEC 60093 |
Relative Permittivity (23°C, 1 MHz) |
3.80
|
--
|
IEC 60250 | |
Dissipation Factor | IEC 60250 | |||
23°C, 100 Hz
|
0.018
|
--
|
||
23°C, 1 MHz
|
0.018
|
--
|
||
Comparative Tracking Index |
285
|
--
|
V
|
IEC 60112 |
Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flame Rating - UL | UL 94 | |||
0.350 mm
|
V-0
|
--
|
||
0.750 mm
|
V-0
|
--
|
||
1.50 mm
|
5VA
|
--
|
||
3.00 mm
|
5VA
|
--
|
||
Flammability Classification | IEC 60695-11-10, -20 | |||
0.350 mm
|
V-0
|
--
|
||
0.750 mm
|
V-0
|
--
|
||
1.50 mm
|
|
--
|
||
3.00 mm
|
V-0
|
--
|
||
Glow Wire Flammability Index | IEC 60695-2-12 | |||
0.750 mm
|
960
|
--
|
°C
|
|
1.50 mm
|
960
|
--
|
°C
|
|
3.00 mm
|
960
|
--
|
°C
|
|
Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
0.750 mm
|
900
|
--
|
°C
|
|
1.50 mm
|
900
|
--
|
°C
|
|
3.00 mm
|
930
|
--
|
°C
|
|
UL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
RTI Str | UL 746 | |||
0.750 mm
|
105
|
--
|
°C
|
|
1.50 mm
|
115
|
--
|
°C
|
|
3.00 mm
|
120
|
--
|
°C
|
|
RTI Imp | UL 746 | |||
0.750 mm
|
105
|
--
|
°C
|
|
1.50 mm
|
115
|
--
|
°C
|
|
3.00 mm
|
115
|
--
|
°C
|
|
RTI Elec | UL 746 | |||
0.750 mm
|
130
|
--
|
°C
|
|
1.50 mm
|
130
|
--
|
°C
|
|
3.00 mm
|
130
|
--
|
°C
|
|
Comparative Tracking Index (CTI) (PLC) |
PLC 2
|
--
|
UL 746 |
PA66 FR50价格 PA66 FR50英文物性表