| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Specific Gravity |
1.04
|
--
|
g/cm³
|
ASTM D792 |
| Density |
1.04
|
--
|
g/cm³
|
ISO 1183 |
| Molding Shrinkage - Flow (3.20 mm) |
1.8
|
--
|
%
|
Internal Method |
| Molding Shrinkage - Across Flow (3.20 mm) |
1.8
|
--
|
%
|
Internal Method |
| Molding Shrinkage - Flow (2.00 mm) |
1.8
|
--
|
%
|
ISO 294-4 |
| Water Absorption (23°C, 24 hr) |
1.5
|
--
|
%
|
ASTM D570 |
| Water Absorption (Saturation, 23°C) |
6.8
|
--
|
%
|
ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) |
2.3
|
--
|
%
|
ISO 62 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Tensile Modulus (23°C) |
900
|
400
|
MPa
|
ISO 527-2 |
| Tensile Strength (23°C) |
48.0
|
41.0
|
MPa
|
ASTM D638 |
| Tensile Stress (Yield, 23°C) |
31.0
|
--
|
MPa
|
ISO 527-2 |
| Tensile Strain (Yield, 23°C) |
29
|
--
|
%
|
ISO 527-2 |
| Tensile Elongation (Break, 23°C) |
> 230
|
> 230
|
%
|
ASTM D638 |
| Nominal Tensile Strain at Break (23°C) |
> 50
|
> 50
|
%
|
ISO 527-2 |
| Flexural Modulus (23°C) |
524
|
297
|
MPa
|
ASTM D790 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
|
-30°C
|
14
|
13
|
kJ/m²
|
|
|
23°C
|
71
|
130
|
kJ/m²
|
|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
|
-30°C
|
No Break
|
No Break
|
||
|
23°C
|
No Break
|
No Break
|
||
| Notched Izod Impact | ASTM D256 | |||
|
-40°C
|
690
|
--
|
J/m
|
|
|
-20°C
|
800
|
--
|
J/m
|
|
|
0°C
|
1200
|
--
|
J/m
|
|
|
23°C
|
No Break
|
--
|
||
| Tensile Impact Strength 2 (23°C) |
1310
|
1360
|
kJ/m²
|
ASTM D1822 |
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Rockwell Hardness | ASTM D785 | |||
|
M-Scale
|
--
|
57
|
||
|
R-Scale
|
--
|
70
|
||
| Durometer Hardness (Shore D) |
70
|
57
|
ASTM D2240 | |
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) |
170
|
--
|
°C
|
ASTM D648 |
| Heat Deflection Temperature (0.45 MPa, Unannealed) |
170
|
--
|
°C
|
ISO 75-2/B |
| Deflection Temperature Under Load (1.8 MPa, Unannealed) |
52.0
|
--
|
°C
|
ASTM D648 |
| Heat Deflection Temperature (1.8 MPa, Unannealed) |
47.0
|
--
|
°C
|
ISO 75-2/A |
| Melting Temperature |
216
|
--
|
°C
|
ASTM D3418 |
| Melting Temperature 3 |
218
|
--
|
°C
|
ISO 11357-3 |
| CLTE - Flow (23 to 55°C) |
0.00013
|
--
|
cm/cm/°C
|
ASTM D696 |
| CLTE - Flow (23 to 55°C) |
0.00020
|
--
|
cm/cm/°C
|
ASTM E831 |
| CLTE - Flow (23 to 55°C) |
0.00020
|
--
|
cm/cm/°C
|
ISO 11359-2 |
| CLTE - Transverse (23 to 55°C) |
0.00018
|
--
|
cm/cm/°C
|
ASTM E831 |
| CLTE - Transverse (23 to 55°C) |
0.00018
|
--
|
cm/cm/°C
|
ISO 11359-2 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Flame Rating - UL | UL 94 | |||
|
0.750 mm
|
HB
|
--
|
||
|
1.50 mm
|
HB
|
--
|
||
|
3.00 mm
|
HB
|
--
|
||
| Flammability Classification | IEC 60695-11-10, -20 | |||
|
0.750 mm
|
HB
|
--
|
||
|
1.50 mm
|
HB
|
--
|
||
|
3.00 mm
|
HB
|
--
|
||
| UL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| RTI Str | UL 746 | |||
|
0.750 mm
|
95.0
|
--
|
°C
|
|
|
1.50 mm
|
100
|
--
|
°C
|
|
|
3.00 mm
|
110
|
--
|
°C
|
|
| RTI Imp | UL 746 | |||
|
0.750 mm
|
65.0
|
--
|
°C
|
|
|
1.50 mm
|
105
|
--
|
°C
|
|
|
3.00 mm
|
105
|
--
|
°C
|
|
| RTI Elec | UL 746 | |||
|
0.750 mm
|
130
|
--
|
°C
|
|
|
1.50 mm
|
130
|
--
|
°C
|
|
|
3.00 mm
|
130
|
--
|
°C
|
|
| Comparative Tracking Index (CTI) |
> 600
|
--
|
V
|
UL 746 |
ST811HS价格 PA66 ST811HS英文物性