Physical |
Nominal Value
|
Unit
|
Test Method
|
Density
|
1.20
|
g/cm³
|
ISO 1183 |
Apparent Density 2
|
0.66
|
g/cm³
|
ISO 60 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)
|
20
|
g/10 min
|
ISO 1133 |
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)
|
19.0
|
cm³/10min
|
ISO 1133 |
Molding Shrinkage
|
|||
Across Flow
|
0.50 to 0.70
|
%
|
ISO 2577 |
Flow
|
0.50 to 0.70
|
%
|
ISO 2577 |
Across Flow: 2.00 mm 3
|
0.70
|
%
|
ISO 294-4 |
Flow: 2.00 mm 3
|
0.65
|
%
|
ISO 294-4 |
Water Absorption (Saturation, 23°C)
|
0.30
|
%
|
ISO 62 |
Water Absorption (Equilibrium, 23°C, 50% RH)
|
0.12
|
%
|
ISO 62 |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Modulus (23°C)
|
2400
|
MPa
|
ISO 527-2/1 |
Tensile Stress (Yield, 23°C)
|
65.0
|
MPa
|
ISO 527-2/50 |
Tensile Stress (Break, 23°C)
|
70.0
|
MPa
|
ISO 527-2/50 |
Tensile Strain (Yield, 23°C)
|
6.1
|
%
|
ISO 527-2/50 |
Tensile Strain (Break, 23°C)
|
130
|
%
|
ISO 527-2/50 |
Nominal Tensile Strain at Break (23°C)
|
> 50
|
%
|
ISO 527-2/50 |
Tensile Creep Modulus (1 hr)
|
2200
|
MPa
|
ISO 899-1 |
Tensile Creep Modulus (1000 hr)
|
1900
|
MPa
|
ISO 899-1 |
Flexural Modulus 4 (23°C)
|
2350
|
MPa
|
ISO 178 |
Flexural Strength 4
|
ISO 178 | ||
3.5% Strain, 23°C
|
73.0
|
MPa
|
|
23°C
|
97.0
|
MPa
|
|
Flexural Strain at Flexural Strength 5 (23°C)
|
7.1
|
%
|
ISO 178 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Charpy Notched Impact Strength 6
|
ISO 179/1eA | ||
-30°C, Complete Break
|
14
|
kJ/m²
|
|
23°C, Partial Break
|
65
|
kJ/m²
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | ||
-60°C
|
No Break
|
||
-30°C
|
No Break
|
||
23°C
|
No Break
|
||
Notched Izod Impact Strength 7
|
ISO 180/A | ||
-30°C, Complete Break
|
12
|
kJ/m²
|
|
23°C, Partial Break
|
75
|
kJ/m²
|
|
Multi-Axial Instrumented Impact Energy
|
ISO 6603-2 | ||
-30°C
|
65.0
|
J
|
|
23°C
|
55.0
|
J
|
|
Multi-Axial Instrumented Impact Peak Force
|
ISO 6603-2 | ||
-30°C
|
6000
|
N
|
|
23°C
|
5100
|
N
|
|
Hardness |
Nominal Value
|
Unit
|
Test Method
|
Ball Indentation Hardness
|
115
|
MPa
|
ISO 2039-1 |
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Heat Deflection Temperature (0.45 MPa, Unannealed)
|
139
|
°C
|
ISO 75-2/B |
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
125
|
°C
|
ISO 75-2/A |
Glass Transition Temperature 8
|
146
|
°C
|
ISO 11357-2 |
Vicat Softening Temperature
|
|||
--
|
145
|
°C
|
ISO 306/B50 |
--
|
146
|
°C
|
ISO 306/B120 |
Ball Pressure Test (138°C)
|
Pass
|
IEC 60695-10-2 | |
CLTE - Flow (23 to 55°C)
|
0.000065
|
cm/cm/°C
|
ISO 11359-2 |
CLTE - Transverse (23 to 55°C)
|
0.000065
|
cm/cm/°C
|
ISO 11359-2 |
Thermal Conductivity (23°C)
|
0.20
|
W/m/K
|
ISO 8302 |
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Surface Resistivity
|
1.0E+16
|
ohm
|
IEC 60093 |
Volume Resistivity (23°C)
|
1.0E+16
|
ohm·cm
|
IEC 60093 |
Electric Strength (23°C, 1.00 mm)
|
34
|
kV/mm
|
IEC 60243-1 |
Relative Permittivity
|
IEC 60250 | ||
23°C, 100 Hz
|
3.10
|
||
23°C, 1 MHz
|
3.00
|
||
Dissipation Factor
|
IEC 60250 | ||
23°C, 100 Hz
|
0.00050
|
||
23°C, 1 MHz
|
0.0090
|
||
Comparative Tracking Index (Solution A)
|
250
|
V
|
IEC 60112 |
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Oxygen Index 9
|
28
|
%
|
ISO 4589-2 |
Flash Ignition Temperature
|
480
|
°C
|
ASTM D1929 |
Self Ingnition Temperature
|
550
|
°C
|
ASTM D1929 |
Optical |
Nominal Value
|
Unit
|
Test Method
|
Refractive Index 10
|
1.586
|
ISO 489 | |
Transmittance
|
ISO 13468-2 | ||
1000 µm
|
89.0
|
%
|
|
2000 µm
|
89.0
|
%
|
|
3000 µm
|
88.0
|
%
|
|
4000 µm
|
87.0
|
%
|
|
Haze (3000 µm)
|
< 0.80
|
%
|
ISO 14782 |
Additional Information |
Nominal Value
|
Unit
|
Test Method
|
ISO Shortname
|
PC,MR,(,,)-18-9
|
ISO 7391 |
PC 2458价格 PC 2458英文物性 食品级