| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1180
|
kg/m³
|
ISO 1183 2 |
|
Melt volume-flow rate (240°C/5.0 kg)
|
24.0
|
cm³/10min
|
ISO 1133 2 |
|
Molding Shrinkage 3
|
ISO 2577 | ||
|
Across Flow: 240°C, 3.00 mm
|
0.50 to 0.70
|
%
|
|
|
Flow: 240°C, 3.00 mm
|
0.50 to 0.70
|
%
|
|
|
Water Absorption (Saturation)
|
0.50
|
%
|
ISO 62 2 |
|
Water Absorption (Equilibrium)
|
0.20
|
%
|
ISO 62 2 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile modulus
|
2700
|
MPa
|
ISO 527-2 2 |
|
Tensile Stress (Yield)
|
60.0
|
MPa
|
ISO 527-2 2 |
|
Tensile Stress (Break)
|
45.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Strain (Yield)
|
3.5
|
%
|
ISO 527-2 2 |
|
Tensile Strain (Break)
|
> 40
|
%
|
ISO 527-2/50 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact Strength
|
ISO 180/A | ||
|
-30°C
|
10
|
kJ/m²
|
|
|
23°C
|
35
|
kJ/m²
|
|
|
Unnotched Izod Impact Strength (23°C)
|
No Break
|
ISO 180/1U | |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (0.45 MPa)
|
92.0
|
°C
|
ISO 75-2 2 |
|
Deflection Temperature Under Load (1.8 MPa)
|
82.0
|
°C
|
ISO 75-2 2 |
|
Vicat Softening Temperature
|
97.0
|
°C
|
ISO 306/B120 |
|
Vicat Softening Temperature (50°C/h, B (50N))
|
95.0
|
°C
|
ISO 306 2 |
|
CLTE - Flow
|
0.000076
|
cm/cm/°C
|
ISO 11359-2 2 |
|
CLTE - Transverse
|
0.000080
|
cm/cm/°C
|
ISO 11359-2 2 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface resistivity
|
1.0E+16
|
ohm
|
IEC 60093 2 |
|
Volume resistivity
|
1.0E+14
|
ohm·m
|
IEC 60093 2 |
|
Electric strength
|
35
|
kV/mm
|
IEC 60243-1 2 |
|
Relative Permittivity (100 Hz)
|
3.20
|
IEC 60250 2 | |
|
Relative Permittivity (1 MHz)
|
3.10
|
IEC 60250 2 | |
|
Dissipation Factor (100 Hz)
|
0.0050
|
IEC 60250 2 | |
|
Dissipation Factor (1 MHz)
|
0.0060
|
IEC 60250 2 | |
|
Comparative tracking index
|
350
|
IEC 60112 2 | |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
1.50 mm
|
V-0
|
||
|
3.00 mm
|
5VA
|
||
|
2.00 mm
|
5VB
|
||
| Fill Analysis |
Nominal Value
|
Unit
|
Test Method
|
|
Melt Viscosity (260°C, 1000 sec^-1)
|
160
|
Pa·s
|
ISO 11443-A |
FR3000价格 抗紫外线PC/ABS FR3000物性